CARTEC
Description
HIGH TEMPERATURE
High Temperature Gasket
The High Operating Temperature spiral wound gasket utilities high recovery, heat treated Monel spiral wingdings combined with a oxidation inhibited graphite with a high temperature oxidation shield on both inside and outside diameters.
The Mica filler gasket was developed to overcome the problems associated with leakage due to the deterioration of the gasket filler materials at high temperature.
- For use up to 1,000 Centigrade
- Contains no asbestos materials
- Various metallic winding materials are available
- Available with external compression gauge Inner-Ring Type, Outer-Ring Type.
Other Material
Technical Data
General information | Cogemica |
---|---|
Class of mica | Phlogopite |
Binder | silicone resin |
Mica content | ca 90% |
Color | dark green |
Composition Properties | Test Method | Cogemica |
---|---|---|
Phlogopite mica content IEC 371 | - | min 90% |
Silicone Binder content IEC 371-2 | - | max 10% |
Density | IEC 371 | 1.7 g/㎤(+/0.1) (106 Ib/ft³) |
Weight loss | DIN 52911 | < 5% |
Tensile Strength | DIN 52910 | approx. 10N/㎟ |
Compressibility | ASTM F36-J | 25% |
Elastic recovery | ASTM F36-J | 35% |
Creep relaxation 50 Mpa -300 ℃ (7252 psi - 572 ℃) The measurement was performed on Cogemica with a pegged steel insert. | DIN 52913 | 40 N/㎟ |
Dielectric strength | IEC 243 -23℃ | approx. 20kV/㎜ |
Thermal resistance 2 hr to 800℃ | Swelling in thickness | stable |
Max temperature range conitinous | Peaks | 1000℃(1832℉) 1100℃(2012℉ |
Structure of Mica | Mica Flexible Sheet |