LONGITUDINAL SHRINK RATIO | ≤±8% 3:1 Shrink ratio |
OPERATING TEMP. | -45℃~125℃ |
SHRINK TEMP. | 120℃ |
Out jacket flame retardant Super sealing against water, moisture or other contaminants |
Technical Data
Property | Test Method | Standard |
---|---|---|
Tensile Strength (Mpa) | ASTM D2671 | ≥10.4 |
Elongation (%) | ASTM D2671 | ≥300 |
Tensile Strength after aging (Mpa) | UL224 158℃ X 168hr | ≥7.3 |
Elongation after aging (%) | UL224 158℃ X 168hr | ≥200 |
Dielectric Strength (kV/mm) | IEC243 | ≥15 |
Volum resistivity (Ω,cm) | ASTM D876 | ≥1X10¹⁴ |
Hot Melt Adhesive Property
Property | Test Method | Stantard |
---|---|---|
Water absorption | ASTM D570 | ≤0.2% |
Sofening point | ASTM E8 | 95℃ |
Strength of pearing (PE) | ASTM D1000 | 120N/25mm |
Strength of pearing (AL) | ASTM D1000 | 80N/25mm |
Standard Size Dimensions
Size | As supplied | After Recovered(mm) | Standard Package (M/Spool) | |||
inch | mm | Internal Diameter(mm) | Internal Diameter | Total wall Thickness | Wall Thickness of Adhesive | |
1/8 | 3.2 | 3.2 | 1.00 | 0.09±0.15 | 0.35±0.10 | 200 |
3/16 | 4.8 | 4.8 | 1.60 | 1.00±0.15 | 0.40±0.10 | 100 |
1/4 | 6.4 | 6.4 | 2.20 | 1.25±0.15 | 0.45±0.12 | 100 |
5/16 | 7.9 | 7.9 | 2.70 | 1.30±0.15 | 0.50±0.12 | 100 |
3/8 | 9.5 | 9.5 | 3.20 | 1.40±0.15 | 0.50±0.12 | 50 |
1/2 | 12.7 | 12.7 | 4.20 | 1.70±0.15 | 0.50±0.12 | 36.6 |
5/8 | 15.0 | 15.0 | 5.20 | 1.80±0.15 | 0.55±0.15 | 30.5 |